Method of manufacturing NAND flash memory device

ABSTRACT

A method of manufacturing a NAND flash memory device is disclosed. A semiconductor substrate of a portion in which a source select line SSL and a drain select line DSL will be formed is recessed selectively or entirely to a predetermined depth. Accordingly, the channel length of a gate can be increased and disturbance can be reduced. It is therefore possible to improve the reliability and yield of devices.

BACKGROUND

1. Field of the Invention

The invention relates, in general, to a method of manufacturing a NAND flash memory device and, more particularly, to a method of manufacturing a NAND flash memory device, wherein program disturbance can be improved.

2. Discussion of Related Art

A NAND flash memory has a string structure in which source select line (SSL) and drain select line (DSL) gates and 16 to 64 cell gates are arranged in series between a source line and a bit line. The source select line (SSL) and drain select line (DSL) gates are generally greater than the cell gates. The number of cell gates arranged in the first string is generally 32 due to the limit of a cell current.

The cell program of the flash memory device is performed in such a manner that a voltage of 15V to 20V is applied to a selected cell gate and a pass voltage (Vpass) of about 10V is applied to a non-selected cell gate so that carriers introduced into the bit line pass through the gate insulating layer of the selected cell gate and charge the floating gate.

In general, the NAND flash memory device employs a method of applying 0V to the bit line in order to improve the charge efficiency of a selected channel and self-boosting a non-selected channel in order to prohibit program disturbance.

If the level of integration increases and the gate design rules are complicated, however, GIDL (gate induced drain leakage) is generated at the drain of the drain select line DSL or the source select line SSL of a non-selected cell string at the time of the self-boosting operation. Accordingly, program disturbance occurs in which unwanted electrons are injected into neighboring memory cells and the cells are programmed. This results in an abrupt decrease in the reliability and yield of devices.

If the distance between the source select line SSL and the drain select line DSL and neighboring memory cells is sufficiently secured, program disturbance can be controlled up to 90 nm. It is, however, to difficult to secure a sufficient distance as the level of integration is increased. To solve the problem, a method of reducing the size of the drain select line DSL and the source select line SSL has been proposed.

If the size of the source select line SSL is reduced, however, a punch-off leakage current is caused between a boosting channel of a non-selected bit line and a common source at the time of program. This causes to lower the channel boosting level, leading to aggravated program disturbance.

Furthermore, if the size of the drain select line DSL is reduced, the threshold voltage Vt of the drain select transistor is lowered. Accordingly, the channel precharge voltage level is lowered and the boosting level is lowered, resulting in aggravated program disturbance.

SUMMARY OF THE INVENTION

In one embodiment, the invention relates to a method of manufacturing a NAND flash memory device, in which a semiconductor substrate of a source select line SSL, a drain select line DSL, a source line, and a bit line are recessed to a predetermined depth selectively or entirely, thus increasing the effective channel length of a gate and also reducing program disturbance.

According to one aspect, the invention provides a method of manufacturing a NAND flash memory device, including the step of selectively or entirely recessing a portion in which a source select line and a drain select line of a semiconductor substrate will be formed selectively or entirely to a predetermined depth.

According to another aspect, the invention provides a method of manufacturing a NAND flash memory device, including the steps of selectively or entirely recessing a portion in which a source select line and a drain select line of a semiconductor substrate will be formed and then performing annealing, depositing a gate insulating layer, a first polysilicon layer for a floating gate, and a first hard mask layer on the recessed semiconductor substrate to a predetermined thickness, and then etching predetermined regions to form trenches, depositing a first insulating layer on the entire surface so that the trenches are buried, and stripping the first insulating layer to expose a top surface of the first hard mask layer, thereby forming isolation structures, and depositing a second polysilicon layer for a floating gate on the entire surface and then etching predetermined regions.

According to still another aspect, the invention provides a method of manufacturing a NAND flash memory device, including the steps of etching predetermined regions of a semiconductor substrate to form trenches, and then depositing a first insulating layer on the entire surface so that the trenches are buried, stripping the first insulating layer to expose a top surface of the semiconductor substrate, forming isolation structures, selectively or entirely recessing a portion in which a source select line and a drain select line of the semiconductor substrate will be formed and then performing annealing, and depositing a gate insulating layer and a second polysilicon layer for a floating gate on the entire surface and then etching predetermined regions of the second polysilicon layer for a floating gate and the gate insulating layer so that a top surface of the isolation structures is exposed.

BRIEF DESCRIPTION OF THE DRAWINGS

A more complete appreciation of the invention, and many of the attendant advantages thereof, will be readily apparent as the same becomes better understood by reference to the following detailed description when considered in conjunction with the accompanying drawings in which like reference symbols indicate the same or similar components, wherein:

FIG. 1 is a layout diagram illustrating a method of manufacturing a NAND flash memory device employing self-aligned STI (shallow trench isolation) according to a first embodiment of the invention;

FIGS. 2A to 2F are cross-sectional views of the NAND flash memory device taken along line A-A in FIG. 1;

FIGS. 3A to 3F are cross-sectional views of the NAND flash memory device taken along line B-B in FIG. 1;

FIG. 4 is a layout diagram illustrating a method of manufacturing a NAND flash memory device employing common STI according to a second embodiment of the invention;

FIGS. 5A to 5E are cross-sectional views of the NAND flash memory device taken along line C-C in FIG. 4; and

FIGS. 6A to 6E are cross-sectional views of the NAND flash memory device taken along line D-D in FIG. 4.

DETAILED DESCRIPTION OF EMBODIMENTS

The invention will now be described in detail in connection with certain exemplary embodiments with reference to the accompanying drawings.

FIG. 1 is a layout diagram illustrating a method of manufacturing a NAND flash memory device employing self-aligned STI according to a first embodiment of the invention.

A portion in which a source select line SSL and a drain select line DSL of a semiconductor substrate will be formed is recessed (indicated by 10 r) to a predetermined thickness. Active regions 10 a and field regions 10 b are defined by isolation structures formed in predetermined regions of the semiconductor substrate.

Second polysilicon layer for a floating gates 10 c are formed in the active regions 10 a, and second polysilicon layer layers 10 d are formed on the second polysilicon layer for a floating gates 10 c to overlap with the field regions 10 b. Dielectric layers 10 e are formed on the second polysilicon layer layers 10 d. A control gate 10 f is defined to cross the active regions 10 a and the field regions 10 b. The second polysilicon layer for a floating gates 10 c and the second polysilicon layer layers 10 d are patterned using the control gate 10 f as a mask, thus forming a floating gate.

FIGS. 2A to 2F are cross-sectional views of the NAND flash memory device taken along line A-A in FIG. 1, and FIGS. 3A to 3F are cross-sectional views of the NAND flash memory device taken along line B-B in FIG. 1.

Referring to FIGS. 2A and 3A, to increase the threshold voltage Vt of the source select line SSL and the drain select line DSL, an ion implantation process is performed on the portion in which the source select line SSL and the drain select line DSL of a semiconductor substrate 100 will be formed. Accordingly, the threshold voltage Vt of the source select line SSL and the drain select line DSL becomes higher than the threshold voltage Vt of a cell.

A mask (not shown) is formed at a predetermined region on the semiconductor substrate 100. The portion in which the source select line SSL and the drain select line DSL of the semiconductor substrate 100 will be formed is recessed (indicated by “102” in FIG. 3A) using the mask. The recess 102 may be formed by using a mixed gas in which additive gases, such as HBr, Ar, and He, for example, are added to Cl₂ and plasma energy of 100 W to 3 KW, for example. The recessed regions are formed only at the portions in which the source select line SSL and the drain select line DSL will be formed. Accordingly, they are not shown in FIG. 2A, but are shown only in FIG. 3A.

In this case, at the time of the recess (102) process, the semiconductor substrate 100 is damaged. To restore the damaged semiconductor substrate 100, annealing may be performed in a furnace at a low booting temperature of 850° C. to 1500° C., for example.

Referring to FIGS. 2B and 3B, a gate insulating layer 104, a first polysilicon layer for a floating gate 106, and a first hard mask layer 108 are sequentially formed on the recessed semiconductor substrate 100.

Referring to FIGS. 2C and 3C, predetermined regions of the first hard mask layer 108 and the first polysilicon layer for a floating gate 106 are etched. Portions of the gate insulating layer 104 and the semiconductor substrate 100 are etched using the first hard mask layer 108 and the first polysilicon layer for a floating gate 106 as masks, forming trenches (not shown).

A first insulating layer is deposited on the entire surface so that the trenches are buried. The first insulating layer may preferably be formed to a thickness of 300 Å to 10000 Å using a single layer, such as HDP (high density plasma), BPSG (boro-phosphorous silicate glass) or SOG (spin on glass), for example, or a stack layer of the HDP, BPSG, and SOG.

The first insulating layer is then stripped to exposed a top surface of the first hard mask layer 108. The process of stripping the first insulating layer may preferably use CMP (chemical mechanical polishing) or etch back. The first hard mask layer 108 is stripped using a liquefied chemical to form isolation structures 110 (seen in FIG. 2C) having a nipple. Accordingly, the field regions A and the active regions B are defined. The isolation structures 110 are formed in the field regions and are not shown in FIG. 3C accordingly.

Referring to FIGS. 2D and 3D, a second polysilicon layer for a floating gate 112 is deposited on the entire surface. A predetermined region of the second polysilicon layer for a floating gate 112 is etched. An IPO (inter-poly oxide) dielectric layer 114 is deposited on the entire surface. The dielectric layer 114 may be an ONO layer.

Referring to FIGS. 2E and 3E, a predetermined region of the dielectric layer 114 formed in the source select line (SSL) and the drain select line (DSL) regions is stripped. The dielectric layer 114 is stripped by dry etch. This is because if the dielectric layer 114 is stripped by wet etch, gates next to the gates of the source select line SSL and the drain select line DSL may be attacked and the controllability of the process may become low.

A conductive layer for a control gate is formed on the entire surface, forming a control gate. It is preferred that the conductive layer for the control gate is formed by depositing a second polysilicon layer layer 116, a tungsten layer or a tungsten silicide film 118, and a second hard mask layer 120 and etching the second polysilicon layer layer 116, the tungsten layer or the tungsten silicide film 118, and the second hard mask layer 120 so that the conductive layer consists of the tungsten layer or the tungsten silicide film 118 and the second polysilicon layer layer 116.

The dielectric layer 114, the second polysilicon layer for a floating gate 112, the first polysilicon layer for a floating gate 106, and the gate insulating layer 104 are etched using the control gate as a mask, forming a floating gate comprising the polysilicon layers 112 and 106. A gate 122 having the floating gate, the dielectric layer 114, and the control gate is thereby completed.

A second insulating layer is deposited to bury between the gate 122 and the gate 122. The second insulating layer is etched to form a spacer 124 on the sidewall of the gate 122.

Referring to FIGS. 2F and 3F, a buffer oxide layer 126 and a third insulating layer 128 are deposited on the entire surface. The buffer oxide layer 126 and the third insulating layer 128 undergo dry etch, thus exposing a region in which a source line contact will be formed. The third insulating layer 128 may preferably be formed using a nitride layer at a temperature of 250° C. to 900° C. by means of LP-CVD (low pressure chemical vapor deposition) or PE-CVD (plasma enhanced chemical vapor deposition).

The exposed region is buried and then polished, thus forming plugs 130 (FIG. 3F). The plugs 130 may preferably be formed using polysilicon, tungsten, tungsten nitride or barrier metal (for example, Ti, TiN, CoSi, or Ta).

A channel length can be increased by recessing (indicated by “102”) the portion in which the source select line SSL and the drain select line DSL of the semiconductor substrate 100 will be formed to a predetermined thickness as described above. Accordingly, the channel of a cell that has not been programmed is precharged to Vcc (the power supply voltage)−Vt (the threshold voltage) and is then increased by the self-boosting operation. It is therefore possible to reduce a voltage difference between the gate of the cell and the channel and also to prevent the program disturbance phenomenon in which the cell is programmed.

FIG. 4 is a layout diagram illustrating a method of manufacturing a NAND flash memory device employing common STI according to a second embodiment of the invention.

Referring to FIG. 4, active regions 1 and field regions 2 are defined by isolation structures formed in predetermined regions of a semiconductor substrate. Portions in which a source select line SSL and a drain select line DSL of the semiconductor substrate will be formed are recessed (indicated by “3”) to a predetermined thickness.

A second polysilicon layer for a floating gate 4 is formed in the active region 1 and a dielectric layer 5 is formed on the second polysilicon layer for a floating gate 4. A control gate 6 is defined to cross the active regions 1 and the field regions 2. The second polysilicon layer for a floating gate 4 is patterned using the control gate 6 as a mask, thereby forming a floating gate.

FIGS. 5A to 5E are cross-sectional views of the NAND flash memory device taken along line C-C in FIG. 4, and FIGS. 6A to 6E are cross-sectional views of the NAND flash memory device taken along line D-D in FIG. 4.

Referring to FIGS. 5A and 6A, a portion of a semiconductor substrate 200 is etched to form trenches (not shown). A first insulating layer is deposited on the entire surface so that the trenches are buried. The first insulating layer may preferably be formed to a thickness of 300 Å to 10000 Å by using HDP, BPSG, or SOG, for example.

The first insulating layer is then stripped to expose a top surface of the semiconductor substrate 200, thus forming isolation structures 202 (FIG. 5A). Accordingly, the field regions 1 and the active regions 2 are defined. The strip process of the first insulating layer may preferably be performed using CMP or etch-back, for example.

Referring to FIGS. 5B and 6B, to increase the threshold voltage Vt of the source select line SSL and the drain select line DSL, an ion implantation process is performed on the portions in which the source select line SSL and the drain select line DSL of the semiconductor substrate 200 will be formed. Accordingly, the threshold voltage Vt of the source select line SSL and the drain select line DSL becomes higher than the threshold voltage Vt of a cell.

A mask (not shown) is formed at a predetermined region on the semiconductor substrate 200. The portion in which the source select line SSL and the drain select line DSL of the semiconductor substrate 200 will be formed is recessed (indicated by “204” in FIG. 6B) using the mask. The recess 204 may be preferably formed by using a mixed gas in which additive gases, such as HBr, Ar and He, are added to Cl₂ and plasma energy of 100 W to 3 KW, for example. The recessed regions are formed only at the portion in which the source select line SSL and the drain select line DSL will be formed. Accordingly, they are not shown in FIG. 5B, but are shown only in FIG. 6B.

In this case, at the time of the recess (204) process, the semiconductor substrate 200 is damaged. To restore the damaged semiconductor substrate 200, annealing may preferably be performed in a furnace at a low booting temperature of 850° C. to 1500° C.

Referring to FIGS. 5C and 6C, a gate insulating layer 206 and a second polysilicon layer for a floating gate 208 are deposited on the entire surface. Predetermined regions of the second polysilicon layer for a floating gate 208 and the gate insulating layer 206 are stripped so that a top surface of the isolation structures 202 is exposed.

Referring to FIGS. 5D and 6D, an IPO dielectric layer 210 is deposited on the entire surface. The dielectric layer 210 may preferably be an ONO layer. A predetermined region of the dielectric layer 210 formed in the source select line (SSL) and the drain select line (DSL) regions is stripped. The dielectric layer 210 is stripped by dry etch. If the dielectric layer 210 is stripped by wet etch, gates next to the gates of the source select line SSL and the drain select line DSL may be attacked and the controllability of the process may become low.

A second polysilicon layer layer 212, a tungsten layer or a tungsten silicide film 214, and a hard mask layer 216 are deposited on the entire surface. The second polysilicon layer layer 212, the tungsten layer or the tungsten silicide film 214, and the hard mask layer 216 are etched to form a control gate having the tungsten layer or the tungsten silicide film 214 and the second polysilicon layer layer 212.

The dielectric layer 210, the second polysilicon layer for a floating gate 208, and the gate insulating layer 206 are etched using the control gate as a mask, forming a floating gate having the polysilicon layer 208. A gate 218 comprising the floating gate, the dielectric layer 210, and the control gate is thereby formed.

A second insulating layer is deposited to bury between the gate 218 and the gate 218. The second insulating layer is etched to form a spacer 220 on the sidewall of the gate 218.

Referring to FIGS. 5E and 6E, a buffer oxide layer 222 and a third insulating layer 224 are deposited on the entire surface. The buffer oxide layer 222 and the third insulating layer 224 undergo dry etch, thus exposing a region in which a source line contact will be formed. The third insulating layer 224 may preferably be formed using a nitride layer at a temperature of 250° C. to 900° C. by means of LP-CVD or PE-CVD, for example.

The exposed region is buried and then polished, thus forming plugs 226. The plugs 226 may preferably be formed using polysilicon, tungsten, tungsten nitride or barrier metal (for example, Ti, TiN, CoSi, or Ta).

The channel length can be increased by recessing (204) the portion in which the source select line SSL and the drain select line DSL of the semiconductor substrate 200 will be formed to a predetermined thickness as described above. Accordingly, the channel of a cell that has not been programmed is precharged to Vcc−Vt and is then increased by the self-boosting operation. It is therefore possible to reduce a voltage difference between the gate of the cell and the channel and also to prevent the program disturbance phenomenon in which the cell is programmed.

As described above, according to the invention, a portion in which the source select line SSL and the drain select line DSL will be formed is recessed to a predetermined thickness. Accordingly, the channel length can be increased. Due to this, the channel of a cell that has not been programmed is precharged to Vcc−Vt and is increased by the self-boosting operation. Therefore, the program disturbance phenomenon in which a voltage difference between the gate of a cell and the channel abruptly reduces and the cell is thus programmed can be prevented. Furthermore, the reliability and yield of devices can be improved.

While the invention has been described in connection with practical exemplary embodiments, the invention is not limited to the disclosed embodiments but, to the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims. 

1. A method of manufacturing a NAND flash memory device, the comprising the steps of: providing a semiconductor substrate; and selectively or entirely recessing a portion of the semiconductor substrate in which a source select line and a drain select line will be formed.
 2. The method of claim 1, comprising forming the recessed portion using a mixed gas in which additive gases are added to Cl₂ and using plasma energy of 100 W to 3 KW.
 3. The method of claim 2, wherein said additive gases are selected from the group consisting of HBr, Ar, and He.
 4. A method of manufacturing a NAND flash memory device, the method comprising the steps of: selectively or entirely recessing a portion of a semiconductor substrate in which a source select line and a drain select line will be formed; annealing the semiconductor substrate; depositing a gate insulating layer, a first polysilicon layer for a floating gate, and a first hard mask layer on the recessed semiconductor substrate; etching the first hard mask layer, the first polysilicon layer, the gate insulating and the semiconductor substrate to form trenches; depositing a first insulating layer over the trenches and first hard mask layer to fill the trenches; removing the first insulating layer to form a isolation structures; removing the first hard mask layer; and depositing a second polysilicon layer for the floating gate over the first polysilicon layer and the isolation structures.
 5. The method of claim 4, comprising forming the recessed portion using a mixed gas in which additive gases are added to Cl₂ and using a plasma energy of 100 W to 3 KW.
 6. The method of claim 5, wherein said additive gases are selected from the group consisting of HBr, Ar, and He.
 7. The method of claim 4, comprising annealing process is performed at a temperature of 850° C. to 1500° C.
 8. The method of claim 4, further comprising the steps of: after depositing the second polysilicon layer, etching a portion of the second polysilicon layer; forming a dielectric layer over the entire surface including the etched second polysilicon layer; removing the dielectric layer formed in the source select line and the drain select line; forming a conductive layer for a control gate on the entire surface; and forming gates on the semiconductor substrate by etching from the conductive layer to the gate insulating layer.
 9. The method of claim 4, further comprising the step of performing an ion implantation process on the portion in which the source select line and the drain select line of the semiconductor substrate will be formed before the recess formation process.
 10. A method of manufacturing a NAND flash memory device, the method comprising the steps of: forming isolation structures in a semiconductor substrate; selectively or entirely recessing a portion in which a source select line and a drain select line of the semiconductor substrate will be formed; annealing process the semiconductor substrate; and depositing a gate insulating layer and a polysilicon layer for a floating gate.
 11. The method of claim 10, comprising forming the recessed portion using a mixed gas in which additive gases are added to Cl₂ and using a plasma energy of 100 W to 3 KW.
 12. The method of claim 11, wherein said additive gases are selected from the group consisting of HBr, Ar, and He.
 13. The method of claim 10, comprising performing the annealing at a temperature of 850° C. to 1500° C.
 14. The method of claim 10, further comprising the steps of: after depositing the gate insulating layer and the polysilicon layer for the floating gate, etching a portion of the polysilicon layer and the gate insulating layer so that the isolation structures are exposed; forming a dielectric layer on the entire surface including the etched polysilicon layer; removing the dielectric layer formed in the source select line and the drain select line; forming a conductive layer for a control gate on the entire surface; and forming gates on the semiconductor substrate by etching from the conductive layer to the gate insulating layer.
 15. The method of claim 10, further comprising the step of performing an ion implantation process on the portion in which the source select line and the drain select line of the semiconductor substrate will be formed after the isolation structures are formed.
 16. A NAND flash memory device, comprising: cell gates formed on a semiconductor substrate; a source select line formed on the semiconductor substrate on one side of the cell gates; and a drain select line formed on the semiconductor substrate on the other side of the cell gates, wherein the source select line and the drain select line are formed in a recessed portion of the semiconductor substrate.
 17. The NAND flash memory device of claim 16, wherein the recessed portion is selectively or entirely at which the source select line and the drain select line will be formed. 